Emulsion for Textiles
Our resin emulsion for textiles include acrylic ester, styrene-acrylic, ethylene-vinyl acetate and vinyl acetate types. Used in the manufacture of flocked, non woven and resin-treated fabrics, these emulsions make it possible to produce finished textiles with various desirable characteristics. Our POLYSOL KG products are acrylic heat-sensitive gel emulsions that solidify with the application of heat. We also produce easy-to-use low viscosity emulsions for use as laundry starch, and products that enable manufacture of processed cloth with a stiff texture.
Product List by Applications
Flocked fabrics
| Products | Main ingredients | Solid Content (%) | Viscosity (mPa・s/23°C) | pH | Ionic Charge | MFT (°C) | Characteristics |
| F-390 | Ethylene-vinyl acetate-acrylic ester copolymer | 56.0 | 5,000 | 5.5 | A | 0 | For secondary plastic farbrication, adhesion with rigid PVC, crack resistance at low temp |
| F-445 | Ethylene-acrylic ester copolymer | 41.5 | 4,800 | 6.5 | A | 0 | Adhesion with metal and a variety of plastics, workability |
Nonwoven coating resin finish
| Products | Main ingredients | Solid Content (%) | Viscosity (mPa・s/23°C) | pH | Ionic Charge | MFT (°C) | Characteristics |
| AT-115 | Acrylic ester polymer (self-crosslinking) |
45.0 | 200> | 8.0 | A | 25 | Hardness, acid resistance, alkali resistance |
| AT-351 | Acrylic ester polymer (self-crosslinking) |
45.0 | 200> | 5.0 | A | 40 | Hardness water resistance, solvent resistance |
| AT-550 | Acrylic ester polymer (self-crosslinking) |
45.0 | 150> | 8.5 | A | 56 | Hardness water resistance, solvent resistance, high temperature strength |
| AT-860 | Acrylic ester polymer | 50.0 | 200 | 4.0 | N | 60 | Hardness solvent resistance good miscibility with salt |
| EF-262 | Ethylene-vinyl acetate-acrylic ester copolymer (self cross linking) |
49.0 | 150> | 4.0 | A | 20 | Hardness water resistance, solvent resistance, low formalin |
Cloth coating resin finish
| Products | Main ingredients | Solid Content (%) | Viscosity (mPa・s/23°C) | pH | Ionic Charge | MFT (°C) | Characteristics |
| M-17N | Acrylic ester polymer (self-crosslinking) |
39.0 | 50> | 9.0 | A | 25 | Hardness, high film strength, good mechanical stability |
| S-65 | Vinyl acetate polymer | 50.0 | 1,000 | 6.0 | N | 17 | Hardness, profound processing |
| SH-502 | Vinyl acetate polymer | 49.5 | 100> | 3.0 | N | 15 | Profound processing, low viscosity, softness |